Automotive Grey Cast Iron vs. AISI 305 Stainless Steel
Both automotive grey cast iron and AISI 305 stainless steel are iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is automotive grey cast iron and the bottom bar is AISI 305 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 280 | |
| 170 to 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 200 |
| Elongation at Break, % | 9.6 to 14 | |
| 34 to 45 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 69 to 70 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 140 to 290 | |
| 580 to 710 |
| Tensile Strength: Yield (Proof), MPa | 94 to 200 | |
| 230 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 to 280 | |
| 290 |
| Melting Completion (Liquidus), °C | 1380 to 1390 | |
| 1450 |
| Melting Onset (Solidus), °C | 1340 to 1350 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 480 |
| Thermal Conductivity, W/m-K | 41 to 43 | |
| 16 |
| Thermal Expansion, µm/m-K | 12 to 14 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 to 7.6 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 to 9.1 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 to 3.0 | |
| 16 |
| Density, g/cm3 | 7.5 to 7.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.7 | |
| 3.2 |
| Embodied Energy, MJ/kg | 21 to 24 | |
| 45 |
| Embodied Water, L/kg | 44 to 51 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 25 | |
| 200 to 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 110 | |
| 130 to 320 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 5.2 to 11 | |
| 20 to 25 |
| Strength to Weight: Bending, points | 8.0 to 13 | |
| 20 to 23 |
| Thermal Diffusivity, mm2/s | 11 to 12 | |
| 4.2 |
| Thermal Shock Resistance, points | 4.2 to 8.6 | |
| 13 to 15 |