Automotive Grey Cast Iron vs. AISI 422 Stainless Steel
Both automotive grey cast iron and AISI 422 stainless steel are iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is automotive grey cast iron and the bottom bar is AISI 422 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 280 | |
| 260 to 330 |
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 200 |
| Elongation at Break, % | 9.6 to 14 | |
| 15 to 17 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 69 to 70 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 140 to 290 | |
| 910 to 1080 |
| Tensile Strength: Yield (Proof), MPa | 94 to 200 | |
| 670 to 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 to 280 | |
| 270 |
| Melting Completion (Liquidus), °C | 1380 to 1390 | |
| 1480 |
| Melting Onset (Solidus), °C | 1340 to 1350 | |
| 1470 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 470 |
| Thermal Conductivity, W/m-K | 41 to 43 | |
| 24 |
| Thermal Expansion, µm/m-K | 12 to 14 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 to 7.6 | |
| 4.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 to 9.1 | |
| 5.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 to 3.0 | |
| 11 |
| Density, g/cm3 | 7.5 to 7.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.7 | |
| 3.1 |
| Embodied Energy, MJ/kg | 21 to 24 | |
| 44 |
| Embodied Water, L/kg | 44 to 51 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 25 | |
| 140 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 110 | |
| 1140 to 1910 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 5.2 to 11 | |
| 32 to 38 |
| Strength to Weight: Bending, points | 8.0 to 13 | |
| 26 to 30 |
| Thermal Diffusivity, mm2/s | 11 to 12 | |
| 6.4 |
| Thermal Shock Resistance, points | 4.2 to 8.6 | |
| 33 to 39 |