Automotive Grey Cast Iron vs. C19700 Copper
Automotive grey cast iron belongs to the iron alloys classification, while C19700 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is automotive grey cast iron and the bottom bar is C19700 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 120 |
| Elongation at Break, % | 9.6 to 14 | |
| 2.4 to 13 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 69 to 70 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 140 to 290 | |
| 400 to 530 |
| Tensile Strength: Yield (Proof), MPa | 94 to 200 | |
| 330 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 to 280 | |
| 210 |
| Melting Completion (Liquidus), °C | 1380 to 1390 | |
| 1090 |
| Melting Onset (Solidus), °C | 1340 to 1350 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 390 |
| Thermal Conductivity, W/m-K | 41 to 43 | |
| 250 |
| Thermal Expansion, µm/m-K | 12 to 14 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 to 7.6 | |
| 86 to 88 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 to 9.1 | |
| 87 to 89 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 to 3.0 | |
| 30 |
| Density, g/cm3 | 7.5 to 7.6 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 21 to 24 | |
| 41 |
| Embodied Water, L/kg | 44 to 51 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 25 | |
| 12 to 49 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 110 | |
| 460 to 1160 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 5.2 to 11 | |
| 12 to 16 |
| Strength to Weight: Bending, points | 8.0 to 13 | |
| 14 to 16 |
| Thermal Diffusivity, mm2/s | 11 to 12 | |
| 73 |
| Thermal Shock Resistance, points | 4.2 to 8.6 | |
| 14 to 19 |