Automotive Grey Cast Iron vs. C26800 Brass
Automotive grey cast iron belongs to the iron alloys classification, while C26800 brass belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is automotive grey cast iron and the bottom bar is C26800 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 110 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 69 to 70 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 140 to 290 | |
| 310 to 650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 to 280 | |
| 180 |
| Melting Completion (Liquidus), °C | 1380 to 1390 | |
| 930 |
| Melting Onset (Solidus), °C | 1340 to 1350 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 390 |
| Thermal Conductivity, W/m-K | 41 to 43 | |
| 120 |
| Thermal Expansion, µm/m-K | 12 to 14 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 to 7.6 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 to 9.1 | |
| 30 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 to 3.0 | |
| 24 |
| Density, g/cm3 | 7.5 to 7.6 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 21 to 24 | |
| 45 |
| Embodied Water, L/kg | 44 to 51 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 5.2 to 11 | |
| 11 to 22 |
| Strength to Weight: Bending, points | 8.0 to 13 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 11 to 12 | |
| 37 |
| Thermal Shock Resistance, points | 4.2 to 8.6 | |
| 10 to 22 |