Automotive Grey Cast Iron vs. C66300 Brass
Automotive grey cast iron belongs to the iron alloys classification, while C66300 brass belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is automotive grey cast iron and the bottom bar is C66300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 110 |
| Elongation at Break, % | 9.6 to 14 | |
| 2.3 to 22 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 69 to 70 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 140 to 290 | |
| 460 to 810 |
| Tensile Strength: Yield (Proof), MPa | 94 to 200 | |
| 400 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 to 280 | |
| 200 |
| Melting Completion (Liquidus), °C | 1380 to 1390 | |
| 1050 |
| Melting Onset (Solidus), °C | 1340 to 1350 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 380 |
| Thermal Conductivity, W/m-K | 41 to 43 | |
| 110 |
| Thermal Expansion, µm/m-K | 12 to 14 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 to 7.6 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 to 9.1 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 to 3.0 | |
| 29 |
| Density, g/cm3 | 7.5 to 7.6 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 21 to 24 | |
| 46 |
| Embodied Water, L/kg | 44 to 51 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 25 | |
| 17 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 110 | |
| 710 to 2850 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 5.2 to 11 | |
| 15 to 26 |
| Strength to Weight: Bending, points | 8.0 to 13 | |
| 15 to 22 |
| Thermal Diffusivity, mm2/s | 11 to 12 | |
| 32 |
| Thermal Shock Resistance, points | 4.2 to 8.6 | |
| 16 to 28 |