Automotive Malleable Cast Iron vs. SAE-AISI 12L14 Steel
Both automotive malleable cast iron and SAE-AISI 12L14 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is automotive malleable cast iron and the bottom bar is SAE-AISI 12L14 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 to 290 | |
| 140 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 190 |
| Elongation at Break, % | 1.0 to 10 | |
| 11 to 25 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 70 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 720 | |
| 440 to 620 |
| Tensile Strength: Yield (Proof), MPa | 220 to 590 | |
| 260 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 41 | |
| 51 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 1.8 |
| Density, g/cm3 | 7.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 20 | |
| 18 |
| Embodied Water, L/kg | 45 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.8 to 30 | |
| 64 to 93 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 950 | |
| 180 to 560 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 26 | |
| 15 to 22 |
| Strength to Weight: Bending, points | 14 to 24 | |
| 16 to 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 14 |
| Thermal Shock Resistance, points | 9.9 to 21 | |
| 14 to 20 |
Alloy Composition
| Carbon (C), % | 2.2 to 2.9 | |
| 0 to 0.15 |
| Iron (Fe), % | 93.6 to 96.7 | |
| 97.9 to 98.7 |
| Lead (Pb), % | 0 | |
| 0.15 to 0.35 |
| Manganese (Mn), % | 0.15 to 1.3 | |
| 0.85 to 1.2 |
| Phosphorus (P), % | 0.020 to 0.15 | |
| 0.040 to 0.090 |
| Silicon (Si), % | 0.9 to 1.9 | |
| 0 |
| Sulfur (S), % | 0.020 to 0.2 | |
| 0.26 to 0.35 |