Beryllia vs. Cesium Bromide
Beryllia belongs to the oxide-based engineering ceramics classification, while cesium bromide belongs to the non-glass optical ceramics. There are 10 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is beryllia and the bottom bar is cesium bromide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.9 | |
| 4.4 |
| Elastic (Young's, Tensile) Modulus, GPa | 350 | |
| 16 |
| Poisson's Ratio | 0.26 | |
| 0.28 |
| Shear Modulus, GPa | 180 | |
| 7.5 |
| Specific Heat Capacity, J/kg-K | 1050 | |
| 270 |
| Stiffness to Weight: Axial, points | 67 | |
| 2.0 |
| Stiffness to Weight: Bending, points | 82 | |
| 19 |
| Thermal Conductivity, W/m-K | 270 | |
| 0.9 |
| Thermal Diffusivity, mm2/s | 89 | |
| 0.76 |
| Thermal Expansion, µm/m-K | 8.0 | |
| 48 |