Boron Carbide vs. Zinc Sulfide
Boron carbide belongs to the non-oxide engineering ceramics classification, while zinc sulfide belongs to the non-glass optical ceramics. There are 9 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is boron carbide and the bottom bar is zinc sulfide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.1 to 2.7 | |
| 4.1 |
| Elastic (Young's, Tensile) Modulus, GPa | 240 to 460 | |
| 75 |
| Poisson's Ratio | 0.17 to 0.19 | |
| 0.28 |
| Specific Heat Capacity, J/kg-K | 950 | |
| 520 |
| Stiffness to Weight: Axial, points | 63 to 100 | |
| 10 |
| Stiffness to Weight: Bending, points | 91 to 100 | |
| 34 |
| Thermal Conductivity, W/m-K | 31 to 90 | |
| 27 |
| Thermal Diffusivity, mm2/s | 16 to 38 | |
| 13 |
| Thermal Expansion, µm/m-K | 4.5 to 5.6 | |
| 6.5 |