Carbon-carbon vs. Graphite
Both carbon-carbon and graphite are non-oxide engineering ceramics. There are 13 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is carbon-carbon and the bottom bar is graphite.
Metric UnitsUS Customary Units
Mechanical Properties
Compressive (Crushing) Strength, MPa | 240 | |
90 |
Elastic (Young's, Tensile) Modulus, GPa | 95 | |
21 |
Tensile Strength: Ultimate (UTS), MPa | 19 | |
18 |
Thermal Properties
Maximum Temperature: Corrosion, °C | 350 | |
180 |
Maximum Temperature: Mechanical, °C | 2400 | |
220 |
Thermal Conductivity, W/m-K | 40 | |
6.0 |
Thermal Expansion, µm/m-K | 4.0 | |
4.9 |
Otherwise Unclassified Properties
Density, g/cm3 | 1.7 | |
1.8 |
Common Calculations
Stiffness to Weight: Axial, points | 31 | |
6.7 |
Stiffness to Weight: Bending, points | 89 | |
53 |
Strength to Weight: Axial, points | 3.0 | |
2.9 |
Strength to Weight: Bending, points | 9.1 | |
8.7 |
Thermal Shock Resistance, points | 3.5 | |
12 |