CA vs. POM-C
Both CA and POM-C are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is CA and the bottom bar is POM-C.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.3 | |
| 1.4 to 1.6 |
| Elongation at Break, % | 25 to 30 | |
| 3.0 to 65 |
| Flexural Modulus, GPa | 1.7 to 2.1 | |
| 2.6 to 9.0 |
| Flexural Strength, MPa | 40 to 55 | |
| 83 to 170 |
| Limiting Oxygen Index (LOI), % | 17 | |
| 15 |
| Specific Heat Capacity, J/kg-K | 1500 | |
| 1130 to 1370 |
| Strength to Weight: Axial, points | 6.4 to 7.9 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 17 to 19 | |
| 24 to 32 |
| Tensile Strength: Ultimate (UTS), MPa | 30 to 37 | |
| 61 to 110 |