CA vs. PS
Both CA and PS are thermoplastics. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is CA and the bottom bar is PS.
Metric UnitsUS Customary Units
Mechanical Properties
| Elongation at Break, % | 25 to 30 | |
| 1.8 to 40 |
| Flexural Strength, MPa | 40 to 55 | |
| 62 to 80 |
| Tensile Strength: Ultimate (UTS), MPa | 30 to 37 | |
| 32 to 44 |
Thermal Properties
| Glass Transition Temperature, °C | 230 | |
| 100 |
| Maximum Temperature: Autoignition, °C | 400 | |
| 360 to 420 |
| Maximum Temperature: Decomposition, °C | 250 | |
| 320 to 330 |
| Specific Heat Capacity, J/kg-K | 1500 | |
| 1250 to 1400 |
| Thermal Conductivity, W/m-K | 0.25 | |
| 0.14 to 0.22 |
| Thermal Expansion, µm/m-K | 14 | |
| 80 to 98 |
| Vicat Softening Temperature, °C | 100 to 110 | |
| 100 to 110 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 15 | |
| 18 to 20 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 16 | |
| 14 to 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 | |
| 1.0 |
| Limiting Oxygen Index (LOI), % | 17 | |
| 18 |
| Water Absorption After 24 Hours, % | 2.3 | |
| 0.040 to 0.080 |
Common Calculations
| Strength to Weight: Axial, points | 6.4 to 7.9 | |
| 8.5 to 12 |
| Strength to Weight: Bending, points | 17 to 19 | |
| 22 to 26 |
| Thermal Diffusivity, mm2/s | 0.13 | |
| 0.11 to 0.15 |