CR Rubber vs. RPU
CR rubber belongs to the thermoset elastomers (rubber) classification, while RPU belongs to the thermoset plastics. There are 10 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is CR rubber and the bottom bar is RPU.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.5 | |
| 1.2 |
| Elongation at Break, % | 380 | |
| 90 |
| Maximum Temperature: Autoignition, °C | 410 | |
| 380 |
| Maximum Temperature: Decomposition, °C | 350 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 1120 | |
| 1750 |
| Strength to Weight: Axial, points | 1.9 | |
| 14 |
| Strength to Weight: Bending, points | 7.1 | |
| 28 |
| Tensile Strength: Ultimate (UTS), MPa | 11 | |
| 60 |
| Thermal Conductivity, W/m-K | 0.19 | |
| 0.19 |
| Thermal Diffusivity, mm2/s | 0.11 | |
| 0.090 |