Chromium 33 vs. Grade 365 Molybdenum

Both chromium 33 and grade 365 molybdenum are otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is chromium 33 and the bottom bar is grade 365 molybdenum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
310
Elongation at Break, % 45
6.3
Poisson's Ratio 0.27
0.31
Shear Modulus, GPa 81
120
Tensile Strength: Ultimate (UTS), MPa 850
620
Tensile Strength: Yield (Proof), MPa 430
530

Thermal Properties

Latent Heat of Fusion, J/g 320
370
Specific Heat Capacity, J/kg-K 480
250
Thermal Expansion, µm/m-K 14
7.0

Otherwise Unclassified Properties

Density, g/cm3 7.9
10
Embodied Carbon, kg CO2/kg material 6.0
28
Embodied Energy, MJ/kg 84
330
Embodied Water, L/kg 250
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 320
37
Resilience: Unit (Modulus of Resilience), kJ/m3 450
450
Stiffness to Weight: Axial, points 14
17
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 30
17
Strength to Weight: Bending, points 25
16
Thermal Shock Resistance, points 21
21

Alloy Composition

Carbon (C), % 0 to 0.015
0 to 0.010
Chromium (Cr), % 31 to 35
0
Copper (Cu), % 0.3 to 1.2
0
Iron (Fe), % 25.7 to 37.9
0 to 0.010
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0.5 to 2.0
99.9 to 100
Nickel (Ni), % 30 to 33
0 to 0.0020
Nitrogen (N), % 0.35 to 0.6
0 to 0.0020
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0 to 0.010
Sulfur (S), % 0 to 0.010
0