Chromium 33 vs. R60704 Alloy
Both chromium 33 and R60704 alloy are otherwise unclassified metals. Both are furnished in the annealed condition. There are 18 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is chromium 33 and the bottom bar is R60704 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
97 |
Elongation at Break, % | 45 | |
16 |
Poisson's Ratio | 0.27 | |
0.34 |
Shear Modulus, GPa | 81 | |
36 |
Tensile Strength: Ultimate (UTS), MPa | 850 | |
470 |
Tensile Strength: Yield (Proof), MPa | 430 | |
270 |
Thermal Properties
Latent Heat of Fusion, J/g | 320 | |
240 |
Specific Heat Capacity, J/kg-K | 480 | |
270 |
Thermal Expansion, µm/m-K | 14 | |
6.0 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.9 | |
6.7 |
Embodied Water, L/kg | 250 | |
460 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
64 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 | |
370 |
Stiffness to Weight: Axial, points | 14 | |
8.1 |
Stiffness to Weight: Bending, points | 25 | |
23 |
Strength to Weight: Axial, points | 30 | |
20 |
Strength to Weight: Bending, points | 25 | |
20 |
Thermal Shock Resistance, points | 21 | |
58 |
Alloy Composition
Carbon (C), % | 0 to 0.015 | |
0 to 0.050 |
Chromium (Cr), % | 31 to 35 | |
0.2 to 0.4 |
Copper (Cu), % | 0.3 to 1.2 | |
0 |
Hafnium (Hf), % | 0 | |
0 to 4.5 |
Hydrogen (H), % | 0 | |
0 to 0.0050 |
Iron (Fe), % | 25.7 to 37.9 | |
0.2 to 0.4 |
Manganese (Mn), % | 0 to 2.0 | |
0 |
Molybdenum (Mo), % | 0.5 to 2.0 | |
0 |
Nickel (Ni), % | 30 to 33 | |
0 |
Nitrogen (N), % | 0.35 to 0.6 | |
0 to 0.025 |
Oxygen (O), % | 0 | |
0 to 0.18 |
Phosphorus (P), % | 0 to 0.020 | |
0 |
Silicon (Si), % | 0 to 0.5 | |
0 |
Sulfur (S), % | 0 to 0.010 | |
0 |
Tin (Sn), % | 0 | |
1.0 to 2.0 |
Zirconium (Zr), % | 0 | |
93 to 98.8 |