Class 1 Tungsten vs. AWS E209
Class 1 tungsten belongs to the otherwise unclassified metals classification, while AWS E209 belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is class 1 tungsten and the bottom bar is AWS E209.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 250 | |
| 200 |
| Elongation at Break, % | 5.7 | |
| 17 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 98 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 860 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 300 |
| Specific Heat Capacity, J/kg-K | 120 | |
| 480 |
| Thermal Expansion, µm/m-K | 5.1 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 15 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 22 | |
| 4.4 |
| Embodied Energy, MJ/kg | 340 | |
| 63 |
| Embodied Water, L/kg | 140 | |
| 180 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.6 | |
| 14 |
| Stiffness to Weight: Bending, points | 14 | |
| 25 |
| Strength to Weight: Axial, points | 16 | |
| 28 |
| Strength to Weight: Bending, points | 14 | |
| 24 |
| Thermal Shock Resistance, points | 48 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.060 |
| Chromium (Cr), % | 0 | |
| 20.5 to 24 |
| Copper (Cu), % | 0 | |
| 0 to 0.75 |
| Iron (Fe), % | 0 | |
| 51.5 to 64.3 |
| Manganese (Mn), % | 0 | |
| 4.0 to 7.0 |
| Molybdenum (Mo), % | 0 | |
| 1.5 to 3.0 |
| Nickel (Ni), % | 0 | |
| 9.5 to 12 |
| Nitrogen (N), % | 0 | |
| 0.1 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 90 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.3 |
| Residuals, % | 10 | |
| 0 |