Class 2 Tungsten vs. EN 1.3553 Steel

Class 2 tungsten belongs to the otherwise unclassified metals classification, while EN 1.3553 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is class 2 tungsten and the bottom bar is EN 1.3553 steel.

Class 2 Tungsten EN 1.3553 (X82WMoCrV6-5-4) High-Temperature Bearing Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		260
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		100
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		860
Tensile Strength: Ultimate (UTS), MPa		720

Thermal Properties

Latent Heat of Fusion, J/g		160
Latent Heat of Fusion, J/g		260

Specific Heat Capacity, J/kg-K		120
Specific Heat Capacity, J/kg-K		440

Thermal Conductivity, W/m-K		20
Thermal Conductivity, W/m-K		24

Thermal Expansion, µm/m-K		4.6
Thermal Expansion, µm/m-K		12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		13
Electrical Conductivity: Equal Volume, % IACS		10

Electrical Conductivity: Equal Weight (Specific), % IACS		7.8
Electrical Conductivity: Equal Weight (Specific), % IACS		11

Otherwise Unclassified Properties

Density, g/cm³		15
Density, g/cm³		8.4

Embodied Carbon, kg CO₂/kg material		23
Embodied Carbon, kg CO₂/kg material		8.5

Embodied Energy, MJ/kg		350
Embodied Energy, MJ/kg		130

Embodied Water, L/kg		140
Embodied Water, L/kg		96

Common Calculations

Stiffness to Weight: Axial, points		9.6
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		14
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		16
Strength to Weight: Axial, points		24

Strength to Weight: Bending, points		13
Strength to Weight: Bending, points		21

Thermal Diffusivity, mm²/s		11
Thermal Diffusivity, mm²/s		6.4

Thermal Shock Resistance, points		52
Thermal Shock Resistance, points		21

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0.78 to 0.86

Chromium (Cr), %		0
Chromium (Cr), %		3.9 to 4.3

Copper (Cu), %		0
Copper (Cu), %		0 to 0.3

Iron (Fe), %		0
Iron (Fe), %		80.7 to 83.7

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.4

Molybdenum (Mo), %		0
Molybdenum (Mo), %		4.7 to 5.2

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.025

Silicon (Si), %		0
Silicon (Si), %		0 to 0.4

Sulfur (S), %		0
Sulfur (S), %		0 to 0.015

Tungsten (W), %		92.5
Tungsten (W), %		6.0 to 6.7

Vanadium (V), %		0
Vanadium (V), %		1.7 to 2.0

Residuals, %		7.5
Residuals, %		0