Class 2 Tungsten vs. CR011A Copper

Class 2 tungsten belongs to the otherwise unclassified metals classification, while CR011A copper belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is class 2 tungsten and the bottom bar is CR011A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 260
120
Elongation at Break, % 5.7
15
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 100
43
Tensile Strength: Ultimate (UTS), MPa 860
220
Tensile Strength: Yield (Proof), MPa 580
130

Thermal Properties

Latent Heat of Fusion, J/g 160
210
Specific Heat Capacity, J/kg-K 120
390
Thermal Conductivity, W/m-K 20
390
Thermal Expansion, µm/m-K 4.6
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
100
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
100

Otherwise Unclassified Properties

Density, g/cm3 15
9.0
Embodied Carbon, kg CO2/kg material 23
2.6
Embodied Energy, MJ/kg 350
42
Embodied Water, L/kg 140
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 44
29
Resilience: Unit (Modulus of Resilience), kJ/m3 640
76
Stiffness to Weight: Axial, points 9.6
7.2
Stiffness to Weight: Bending, points 14
18
Strength to Weight: Axial, points 16
6.8
Strength to Weight: Bending, points 13
9.0
Thermal Diffusivity, mm2/s 11
110
Thermal Shock Resistance, points 52
7.8

Alloy Composition

Bismuth (Bi), % 0
0 to 0.00050
Copper (Cu), % 0
99.88 to 99.97
Oxygen (O), % 0
0 to 0.040
Silver (Ag), % 0
0.030 to 0.050
Tungsten (W), % 92.5
0
Residuals, % 7.5
0