Class 3 Tungsten vs. Automotive Grey Cast Iron
Class 3 tungsten belongs to the otherwise unclassified metals classification, while automotive grey cast iron belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is class 3 tungsten and the bottom bar is automotive grey cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 270 | |
| 180 |
| Elongation at Break, % | 3.4 | |
| 9.6 to 14 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 100 | |
| 69 to 70 |
| Tensile Strength: Ultimate (UTS), MPa | 830 | |
| 140 to 290 |
| Tensile Strength: Yield (Proof), MPa | 580 | |
| 94 to 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 260 to 280 |
| Specific Heat Capacity, J/kg-K | 120 | |
| 490 |
| Thermal Conductivity, W/m-K | 30 | |
| 41 to 43 |
| Thermal Expansion, µm/m-K | 4.5 | |
| 12 to 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 7.4 to 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 8.8 to 9.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 15 | |
| 7.5 to 7.6 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 1.5 to 1.7 |
| Embodied Energy, MJ/kg | 360 | |
| 21 to 24 |
| Embodied Water, L/kg | 150 | |
| 44 to 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 25 | |
| 18 to 25 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 630 | |
| 25 to 110 |
| Stiffness to Weight: Axial, points | 9.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 14 | |
| 25 |
| Strength to Weight: Axial, points | 15 | |
| 5.2 to 11 |
| Strength to Weight: Bending, points | 13 | |
| 8.0 to 13 |
| Thermal Diffusivity, mm2/s | 15 | |
| 11 to 12 |
| Thermal Shock Resistance, points | 49 | |
| 4.2 to 8.6 |