Class 3 Tungsten vs. EN 1.5526 Steel
Class 3 tungsten belongs to the otherwise unclassified metals classification, while EN 1.5526 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is class 3 tungsten and the bottom bar is EN 1.5526 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 270 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 100 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 830 | |
| 490 to 1650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 120 | |
| 470 |
| Thermal Conductivity, W/m-K | 30 | |
| 48 |
| Thermal Expansion, µm/m-K | 4.5 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 8.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 15 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 1.4 |
| Embodied Energy, MJ/kg | 360 | |
| 19 |
| Embodied Water, L/kg | 150 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 15 | |
| 17 to 59 |
| Strength to Weight: Bending, points | 13 | |
| 18 to 40 |
| Thermal Diffusivity, mm2/s | 15 | |
| 13 |
| Thermal Shock Resistance, points | 49 | |
| 14 to 49 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 | |
| 0.27 to 0.32 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 | |
| 97.7 to 98.9 |
| Manganese (Mn), % | 0 | |
| 0.8 to 1.1 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Tungsten (W), % | 95 | |
| 0 |
| Residuals, % | 5.0 | |
| 0 |