Class 3 Tungsten vs. S17400 Stainless Steel
Class 3 tungsten belongs to the otherwise unclassified metals classification, while S17400 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is class 3 tungsten and the bottom bar is S17400 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 270 | |
| 190 |
| Elongation at Break, % | 3.4 | |
| 11 to 21 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Rockwell C Hardness | 30 | |
| 27 to 43 |
| Shear Modulus, GPa | 100 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 830 | |
| 910 to 1390 |
| Tensile Strength: Yield (Proof), MPa | 580 | |
| 580 to 1250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 280 |
| Specific Heat Capacity, J/kg-K | 120 | |
| 480 |
| Thermal Conductivity, W/m-K | 30 | |
| 17 |
| Thermal Expansion, µm/m-K | 4.5 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 2.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 15 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 2.7 |
| Embodied Energy, MJ/kg | 360 | |
| 39 |
| Embodied Water, L/kg | 150 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 25 | |
| 140 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 630 | |
| 880 to 4060 |
| Stiffness to Weight: Axial, points | 9.6 | |
| 14 |
| Stiffness to Weight: Bending, points | 14 | |
| 25 |
| Strength to Weight: Axial, points | 15 | |
| 32 to 49 |
| Strength to Weight: Bending, points | 13 | |
| 27 to 35 |
| Thermal Diffusivity, mm2/s | 15 | |
| 4.5 |
| Thermal Shock Resistance, points | 49 | |
| 30 to 46 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.070 |
| Chromium (Cr), % | 0 | |
| 15 to 17 |
| Copper (Cu), % | 0 | |
| 3.0 to 5.0 |
| Iron (Fe), % | 0 | |
| 70.4 to 78.9 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 3.0 to 5.0 |
| Niobium (Nb), % | 0 | |
| 0.15 to 0.45 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 95 | |
| 0 |
| Residuals, % | 5.0 | |
| 0 |