Class 4 Tungsten vs. Monel R-405
Class 4 tungsten belongs to the otherwise unclassified metals classification, while Monel R-405 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is class 4 tungsten and the bottom bar is Monel R-405.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 270 | |
| 160 |
| Elongation at Break, % | 2.3 | |
| 9.1 to 39 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 110 | |
| 62 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 540 to 630 |
| Tensile Strength: Yield (Proof), MPa | 580 | |
| 190 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 430 |
| Thermal Conductivity, W/m-K | 30 | |
| 23 |
| Thermal Expansion, µm/m-K | 4.5 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 17 | |
| 3.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.7 | |
| 3.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 16 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 24 | |
| 7.9 |
| Embodied Energy, MJ/kg | 360 | |
| 110 |
| Embodied Water, L/kg | 150 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 | |
| 49 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 620 | |
| 120 to 370 |
| Stiffness to Weight: Axial, points | 9.6 | |
| 10 |
| Stiffness to Weight: Bending, points | 14 | |
| 21 |
| Strength to Weight: Axial, points | 14 | |
| 17 to 20 |
| Strength to Weight: Bending, points | 12 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 15 | |
| 5.9 |
| Thermal Shock Resistance, points | 46 | |
| 17 to 20 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 28 to 34 |
| Iron (Fe), % | 0 | |
| 0 to 2.5 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 63 to 72 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0.025 to 0.060 |
| Tungsten (W), % | 97 | |
| 0 |
| Residuals, % | 3.0 | |
| 0 |