Class 4 Tungsten vs. C14180 Copper
Class 4 tungsten belongs to the otherwise unclassified metals classification, while C14180 copper belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is class 4 tungsten and the bottom bar is C14180 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 270 | |
| 120 |
| Elongation at Break, % | 2.3 | |
| 15 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 110 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 210 |
| Tensile Strength: Yield (Proof), MPa | 580 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 210 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 390 |
| Thermal Conductivity, W/m-K | 30 | |
| 370 |
| Thermal Expansion, µm/m-K | 4.5 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 16 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 24 | |
| 2.6 |
| Embodied Energy, MJ/kg | 360 | |
| 41 |
| Embodied Water, L/kg | 150 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 | |
| 28 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 620 | |
| 69 |
| Stiffness to Weight: Axial, points | 9.6 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 14 | |
| 18 |
| Strength to Weight: Axial, points | 14 | |
| 6.5 |
| Strength to Weight: Bending, points | 12 | |
| 8.8 |
| Thermal Diffusivity, mm2/s | 15 | |
| 110 |
| Thermal Shock Resistance, points | 46 | |
| 7.4 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 0 | |
| 99.9 to 100 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 | |
| 0 to 0.075 |
| Tungsten (W), % | 97 | |
| 0 |
| Residuals, % | 3.0 | |
| 0 |