Cold Finished SAE-AISI 8620 vs. Work Hardened 92-silver 8-tin-oxide
Cold finished SAE-AISI 8620 belongs to the iron alloys classification, while work hardened 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is cold finished SAE-AISI 8620 and the bottom bar is work hardened 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 76 |
| Elongation at Break, % | 13 | |
| 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 86 | |
| 110 |
| Shear Strength, MPa | 420 | |
| 210 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 320 |
| Tensile Strength: Yield (Proof), MPa | 570 | |
| 300 |