Cold-rolled Z21210 Zinc vs. Strain Hardened S20910 Stainless Steel
Cold-rolled Z21210 zinc belongs to the zinc alloys classification, while strain hardened S20910 stainless steel belongs to the iron alloys. There are 10 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is cold-rolled Z21210 zinc and the bottom bar is strain hardened S20910 stainless steel.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.1 | |
| 7.8 |
| Melting Completion (Liquidus), °C | 420 | |
| 1420 |
| Melting Onset (Solidus), °C | 420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 480 |
| Strength to Weight: Axial, points | 6.4 | |
| 33 |
| Strength to Weight: Bending, points | 9.4 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 940 |
| Thermal Conductivity, W/m-K | 110 | |
| 13 |
| Thermal Diffusivity, mm2/s | 38 | |
| 3.6 |
| Thermal Expansion, µm/m-K | 32 | |
| 16 |