Cold Worked Monel R-405 vs. Cold Worked Type 4 Magnetic Alloy
Both cold worked Monel R-405 and cold worked Type 4 magnetic alloy are nickel alloys. Both are furnished in the cold worked (strain hardened) condition. They have 70% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is cold worked Monel R-405 and the bottom bar is cold worked Type 4 magnetic alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 190 |
| Elongation at Break, % | 9.1 | |
| 2.0 |
| Fatigue Strength, MPa | 250 | |
| 400 |
| Poisson's Ratio | 0.32 | |
| 0.31 |
| Shear Modulus, GPa | 62 | |
| 73 |
| Shear Strength, MPa | 370 | |
| 630 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 1100 |
| Tensile Strength: Yield (Proof), MPa | 350 | |
| 1040 |
Thermal Properties
| Curie Temperature, °C | 18 | |
| 460 |
| Latent Heat of Fusion, J/g | 270 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 900 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1420 |
| Melting Onset (Solidus), °C | 1300 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 440 |
| Thermal Expansion, µm/m-K | 14 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.4 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.4 | |
| 3.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 60 |
| Density, g/cm3 | 8.9 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 10 |
| Embodied Energy, MJ/kg | 110 | |
| 140 |
| Embodied Water, L/kg | 250 | |
| 210 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 49 | |
| 22 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 2840 |
| Stiffness to Weight: Axial, points | 10 | |
| 12 |
| Stiffness to Weight: Bending, points | 21 | |
| 22 |
| Strength to Weight: Axial, points | 20 | |
| 35 |
| Strength to Weight: Bending, points | 18 | |
| 27 |
| Thermal Shock Resistance, points | 20 | |
| 37 |
Alloy Composition
| Carbon (C), % | 0 to 0.3 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Cobalt (Co), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 28 to 34 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 2.5 | |
| 9.5 to 17.5 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 6.0 |
| Nickel (Ni), % | 63 to 72 | |
| 79 to 82 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0.025 to 0.060 | |
| 0 to 0.020 |