Commercially Pure Zinc vs. C37700 Brass
Commercially pure zinc belongs to the zinc alloys classification, while C37700 brass belongs to the copper alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is commercially pure zinc and the bottom bar is C37700 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 87 | |
| 100 |
| Elongation at Break, % | 38 | |
| 40 |
| Poisson's Ratio | 0.25 | |
| 0.31 |
| Shear Modulus, GPa | 35 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 97 | |
| 400 |
| Tensile Strength: Yield (Proof), MPa | 79 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 90 | |
| 120 |
| Melting Completion (Liquidus), °C | 410 | |
| 890 |
| Melting Onset (Solidus), °C | 400 | |
| 880 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 120 |
| Thermal Expansion, µm/m-K | 26 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 37 | |
| 30 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 23 |
| Density, g/cm3 | 6.6 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.6 |
| Embodied Energy, MJ/kg | 53 | |
| 45 |
| Embodied Water, L/kg | 340 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 34 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 36 | |
| 120 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 4.1 | |
| 14 |
| Strength to Weight: Bending, points | 7.1 | |
| 15 |
| Thermal Diffusivity, mm2/s | 44 | |
| 39 |
| Thermal Shock Resistance, points | 3.0 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.010 | |
| 0 |
| Copper (Cu), % | 0 to 0.080 | |
| 58 to 61 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 to 0.030 | |
| 1.5 to 2.5 |
| Tin (Sn), % | 0 to 0.0030 | |
| 0 |
| Titanium (Ti), % | 0 to 0.020 | |
| 0 |
| Zinc (Zn), % | 99.827 to 100 | |
| 35.7 to 40.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |