Commercially Pure Zirconium vs. ASTM B817 Type I
Commercially pure zirconium belongs to the otherwise unclassified metals classification, while ASTM B817 type I belongs to the titanium alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is commercially pure zirconium and the bottom bar is ASTM B817 type I.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 100 |
| Elongation at Break, % | 18 | |
| 4.0 to 13 |
| Fatigue Strength, MPa | 60 | |
| 360 to 520 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 36 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 770 to 960 |
| Tensile Strength: Yield (Proof), MPa | 240 | |
| 700 to 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 410 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 560 |
| Thermal Conductivity, W/m-K | 22 | |
| 7.1 |
| Thermal Expansion, µm/m-K | 5.5 | |
| 9.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 4.4 |
| Embodied Water, L/kg | 450 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 65 | |
| 30 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 | |
| 2310 to 3540 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 35 |
| Strength to Weight: Axial, points | 18 | |
| 48 to 60 |
| Strength to Weight: Bending, points | 19 | |
| 42 to 49 |
| Thermal Diffusivity, mm2/s | 12 | |
| 2.9 |
| Thermal Shock Resistance, points | 56 | |
| 54 to 68 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 5.5 to 6.8 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.1 |
| Chlorine (Cl), % | 0 | |
| 0 to 0.2 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.4 |
| Nitrogen (N), % | 0 to 0.025 | |
| 0 to 0.040 |
| Oxygen (O), % | 0 to 0.16 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Sodium (Na), % | 0 | |
| 0 to 0.2 |
| Titanium (Ti), % | 0 | |
| 87 to 91 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Zirconium (Zr), % | 94.7 to 100 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |