Commercially Pure Zirconium vs. EN 1.7221 Steel
Commercially pure zirconium belongs to the otherwise unclassified metals classification, while EN 1.7221 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is commercially pure zirconium and the bottom bar is EN 1.7221 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 190 |
| Elongation at Break, % | 18 | |
| 11 to 17 |
| Fatigue Strength, MPa | 60 | |
| 290 to 390 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 36 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 650 to 780 |
| Tensile Strength: Yield (Proof), MPa | 240 | |
| 430 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 470 |
| Thermal Conductivity, W/m-K | 22 | |
| 44 |
| Thermal Expansion, µm/m-K | 5.5 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 7.8 |
| Embodied Water, L/kg | 450 | |
| 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 65 | |
| 83 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 | |
| 490 to 1050 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 23 to 27 |
| Strength to Weight: Bending, points | 19 | |
| 21 to 24 |
| Thermal Diffusivity, mm2/s | 12 | |
| 12 |
| Thermal Shock Resistance, points | 56 | |
| 19 to 23 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.22 to 0.29 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0.8 to 1.2 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 96.8 to 98.3 |
| Manganese (Mn), % | 0 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0.15 to 0.3 |
| Nitrogen (N), % | 0 to 0.025 | |
| 0 |
| Oxygen (O), % | 0 to 0.16 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Zirconium (Zr), % | 94.7 to 100 | |
| 0 |