Commercially Pure Zirconium vs. Grade 365 Molybdenum
Both commercially pure zirconium and grade 365 molybdenum are otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is commercially pure zirconium and the bottom bar is grade 365 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 310 |
| Elongation at Break, % | 18 | |
| 6.3 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 36 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 240 | |
| 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 250 |
| Thermal Expansion, µm/m-K | 5.5 | |
| 7.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.7 | |
| 10 |
| Embodied Water, L/kg | 450 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 65 | |
| 37 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 | |
| 450 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 17 |
| Stiffness to Weight: Bending, points | 23 | |
| 22 |
| Strength to Weight: Axial, points | 18 | |
| 17 |
| Strength to Weight: Bending, points | 19 | |
| 16 |
| Thermal Shock Resistance, points | 56 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0 |
| Hafnium (Hf), % | 0 to 4.5 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0050 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.010 |
| Molybdenum (Mo), % | 0 | |
| 99.9 to 100 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0020 |
| Nitrogen (N), % | 0 to 0.025 | |
| 0 to 0.0020 |
| Oxygen (O), % | 0 to 0.16 | |
| 0 to 0.0015 |
| Silicon (Si), % | 0 | |
| 0 to 0.010 |
| Zirconium (Zr), % | 94.7 to 100 | |
| 0 |