COC vs. PHB
Both COC and PHB are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is COC and the bottom bar is PHB.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.0 | |
| 1.3 |
| Elastic (Young's, Tensile) Modulus, GPa | 3.0 | |
| 1.3 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 14 | |
| 14 |
| Elongation at Break, % | 2.5 | |
| 7.5 |
| Stiffness to Weight: Axial, points | 1.7 | |
| 0.58 |
| Stiffness to Weight: Bending, points | 48 | |
| 29 |
| Strength to Weight: Axial, points | 17 | |
| 6.7 |
| Strength to Weight: Bending, points | 34 | |
| 17 |
| Tensile Strength: Ultimate (UTS), MPa | 60 | |
| 30 |
| Water Absorption After 24 Hours, % | 0 | |
| 0.75 |