R31539 Cobalt vs. EN 1.0599 Steel

R31539 cobalt belongs to the cobalt alloys classification, while EN 1.0599 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is R31539 cobalt and the bottom bar is EN 1.0599 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 13 to 22
20
Fatigue Strength, MPa 310 to 480
310
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 86
73
Tensile Strength: Ultimate (UTS), MPa 1000 to 1340
620
Tensile Strength: Yield (Proof), MPa 590 to 940
440

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1360
1460
Melting Onset (Solidus), °C 1290
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
47
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.5

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.2
1.8
Embodied Energy, MJ/kg 110
24
Embodied Water, L/kg 530
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 190
110
Resilience: Unit (Modulus of Resilience), kJ/m3 780 to 2000
520
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 33 to 44
22
Strength to Weight: Bending, points 27 to 32
21
Thermal Diffusivity, mm2/s 3.5
13
Thermal Shock Resistance, points 24 to 32
20

Alloy Composition

Aluminum (Al), % 0.3 to 1.0
0.010 to 0.050
Carbon (C), % 0 to 0.14
0.16 to 0.22
Chromium (Cr), % 26 to 30
0 to 0.3
Cobalt (Co), % 57.7 to 68.7
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 0 to 0.75
96.1 to 98.4
Lanthanum (La), % 0.030 to 0.2
0
Manganese (Mn), % 0 to 1.0
1.3 to 1.7
Molybdenum (Mo), % 5.0 to 7.0
0 to 0.080
Nickel (Ni), % 0 to 1.0
0 to 0.4
Niobium (Nb), % 0
0 to 0.070
Nitrogen (N), % 0 to 0.25
0 to 0.020
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 1.0
0.1 to 0.5
Sulfur (S), % 0
0 to 0.035
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0.080 to 0.15