Ductile Cast Iron vs. C14510 Copper
Ductile cast iron belongs to the iron alloys classification, while C14510 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ductile cast iron and the bottom bar is C14510 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 170 to 180 | |
| 120 |
| Elongation at Break, % | 2.1 to 20 | |
| 9.1 to 9.6 |
| Poisson's Ratio | 0.28 to 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 64 to 70 | |
| 43 |
| Shear Strength, MPa | 420 to 800 | |
| 180 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 920 | |
| 300 to 320 |
| Tensile Strength: Yield (Proof), MPa | 310 to 670 | |
| 230 to 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 290 | |
| 200 |
| Melting Completion (Liquidus), °C | 1160 | |
| 1080 |
| Melting Onset (Solidus), °C | 1120 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 390 |
| Thermal Conductivity, W/m-K | 31 to 36 | |
| 360 |
| Thermal Expansion, µm/m-K | 11 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 33 |
| Density, g/cm3 | 7.1 to 7.5 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 2.6 |
| Embodied Energy, MJ/kg | 21 | |
| 42 |
| Embodied Water, L/kg | 43 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 17 to 80 | |
| 25 to 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 1330 | |
| 230 to 280 |
| Stiffness to Weight: Axial, points | 12 to 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 to 26 | |
| 18 |
| Strength to Weight: Axial, points | 17 to 35 | |
| 9.2 to 10 |
| Strength to Weight: Bending, points | 18 to 29 | |
| 11 to 12 |
| Thermal Diffusivity, mm2/s | 8.9 to 10 | |
| 100 |
| Thermal Shock Resistance, points | 17 to 35 | |
| 11 to 12 |
Alloy Composition
| Carbon (C), % | 3.0 to 3.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 99.15 to 99.69 |
| Iron (Fe), % | 93.7 to 95.5 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Phosphorus (P), % | 0 to 0.080 | |
| 0.010 to 0.030 |
| Silicon (Si), % | 1.5 to 2.8 | |
| 0 |
| Tellurium (Te), % | 0 | |
| 0.3 to 0.7 |