EN 1.0033 Steel vs. AWS E209

Both EN 1.0033 steel and AWS E209 are iron alloys. They have 58% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.0033 steel and the bottom bar is AWS E209.

EN 1.0033 (E155) Non-Alloy Steel AWS E209 (W32210) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		17 to 32
Elongation at Break, %		17

Poisson's Ratio		0.29
Poisson's Ratio		0.28

Shear Modulus, GPa		73
Shear Modulus, GPa		79

Tensile Strength: Ultimate (UTS), MPa		300 to 330
Tensile Strength: Ultimate (UTS), MPa		770

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		300

Melting Completion (Liquidus), °C		1470
Melting Completion (Liquidus), °C		1420

Melting Onset (Solidus), °C		1420
Melting Onset (Solidus), °C		1370

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		1.8
Base Metal Price, % relative		21

Density, g/cm³		7.9
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		1.4
Embodied Carbon, kg CO₂/kg material		4.4

Embodied Energy, MJ/kg		18
Embodied Energy, MJ/kg		63

Embodied Water, L/kg		45
Embodied Water, L/kg		180

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		10 to 12
Strength to Weight: Axial, points		28

Strength to Weight: Bending, points		13 to 14
Strength to Weight: Bending, points		24

Thermal Shock Resistance, points		9.4 to 10
Thermal Shock Resistance, points		19

Alloy Composition

Carbon (C), %		0 to 0.11
Carbon (C), %		0 to 0.060

Chromium (Cr), %		0
Chromium (Cr), %		20.5 to 24

Copper (Cu), %		0
Copper (Cu), %		0 to 0.75

Iron (Fe), %		98.8 to 100
Iron (Fe), %		51.5 to 64.3

Manganese (Mn), %		0 to 0.7
Manganese (Mn), %		4.0 to 7.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		1.5 to 3.0

Nickel (Ni), %		0
Nickel (Ni), %		9.5 to 12

Nitrogen (N), %		0
Nitrogen (N), %		0.1 to 0.3

Phosphorus (P), %		0 to 0.045
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 0.35
Silicon (Si), %		0 to 1.0

Sulfur (S), %		0 to 0.045
Sulfur (S), %		0 to 0.030

Vanadium (V), %		0
Vanadium (V), %		0.1 to 0.3