EN 1.0033 Steel vs. EN 1.4362 Stainless Steel
Both EN 1.0033 steel and EN 1.4362 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.0033 steel and the bottom bar is EN 1.4362 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 86 to 96 | |
| 230 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 17 to 32 | |
| 25 |
| Fatigue Strength, MPa | 120 to 140 | |
| 320 |
| Poisson's Ratio | 0.29 | |
| 0.27 |
| Shear Modulus, GPa | 73 | |
| 79 |
| Shear Strength, MPa | 200 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 330 | |
| 730 |
| Tensile Strength: Yield (Proof), MPa | 150 to 200 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1060 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1420 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 53 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 14 |
| Density, g/cm3 | 7.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.9 |
| Embodied Energy, MJ/kg | 18 | |
| 41 |
| Embodied Water, L/kg | 45 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 to 83 | |
| 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 63 to 100 | |
| 530 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 10 to 12 | |
| 26 |
| Strength to Weight: Bending, points | 13 to 14 | |
| 23 |
| Thermal Diffusivity, mm2/s | 14 | |
| 4.0 |
| Thermal Shock Resistance, points | 9.4 to 10 | |
| 20 |
Alloy Composition
| Carbon (C), % | 0 to 0.11 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 22 to 24.5 |
| Copper (Cu), % | 0 | |
| 0.1 to 0.6 |
| Iron (Fe), % | 98.8 to 100 | |
| 65.5 to 74.3 |
| Manganese (Mn), % | 0 to 0.7 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 0.1 to 0.6 |
| Nickel (Ni), % | 0 | |
| 3.5 to 5.5 |
| Nitrogen (N), % | 0 | |
| 0.050 to 0.2 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.045 | |
| 0 to 0.015 |