EN 1.0038 Steel vs. ACI-ASTM CN3MN Steel
Both EN 1.0038 steel and ACI-ASTM CN3MN steel are iron alloys. They have 48% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.0038 steel and the bottom bar is ACI-ASTM CN3MN steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 110 to 120 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 23 to 25 | |
| 39 |
| Fatigue Strength, MPa | 140 to 160 | |
| 250 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 430 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 200 to 220 | |
| 300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Conductivity, W/m-K | 49 | |
| 13 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 1.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 33 |
| Density, g/cm3 | 7.8 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 6.2 |
| Embodied Energy, MJ/kg | 19 | |
| 84 |
| Embodied Water, L/kg | 48 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 72 to 88 | |
| 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 130 | |
| 210 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 15 | |
| 21 |
| Strength to Weight: Bending, points | 15 to 16 | |
| 20 |
| Thermal Diffusivity, mm2/s | 13 | |
| 3.4 |
| Thermal Shock Resistance, points | 12 to 13 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0 to 0.23 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 to 0.3 | |
| 20 to 22 |
| Copper (Cu), % | 0 to 0.6 | |
| 0 to 0.75 |
| Iron (Fe), % | 97.1 to 100 | |
| 41.4 to 50.3 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 to 0.080 | |
| 6.0 to 7.0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 23.5 to 25.5 |
| Nitrogen (N), % | 0 to 0.014 | |
| 0.18 to 0.26 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.55 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.045 | |
| 0 to 0.010 |