EN 1.0050 Steel vs. SAE-AISI 1022 Steel
Both EN 1.0050 steel and SAE-AISI 1022 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is EN 1.0050 steel and the bottom bar is SAE-AISI 1022 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 150 | |
| 150 to 160 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 18 | |
| 17 to 26 |
| Fatigue Strength, MPa | 190 | |
| 190 to 300 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 330 | |
| 310 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 530 | |
| 480 to 550 |
| Tensile Strength: Yield (Proof), MPa | 280 | |
| 260 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 53 | |
| 52 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.8 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.8 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.7 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 18 |
| Embodied Water, L/kg | 45 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 | |
| 88 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 | |
| 190 to 530 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 19 | |
| 17 to 19 |
| Strength to Weight: Bending, points | 18 | |
| 17 to 19 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 17 | |
| 15 to 17 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.18 to 0.23 |
| Iron (Fe), % | 99.876 to 100 | |
| 98.7 to 99.12 |
| Manganese (Mn), % | 0 | |
| 0.7 to 1.0 |
| Nitrogen (N), % | 0 to 0.014 | |
| 0 |
| Phosphorus (P), % | 0 to 0.055 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 to 0.055 | |
| 0 to 0.050 |