EN 1.0060 Steel vs. AISI 329 Stainless Steel

Both EN 1.0060 steel and AISI 329 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0060 steel and the bottom bar is AISI 329 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
240
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 13
17
Fatigue Strength, MPa 200
330
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Shear Strength, MPa 380
440
Tensile Strength: Ultimate (UTS), MPa 630
710
Tensile Strength: Yield (Proof), MPa 310
540

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1430
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
16
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
16
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
3.1
Embodied Energy, MJ/kg 18
44
Embodied Water, L/kg 45
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 70
110
Resilience: Unit (Modulus of Resilience), kJ/m3 250
730
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
25
Strength to Weight: Bending, points 21
23
Thermal Diffusivity, mm2/s 14
4.3
Thermal Shock Resistance, points 20
19

Alloy Composition

Carbon (C), % 0
0 to 0.080
Chromium (Cr), % 0
23 to 28
Iron (Fe), % 99.876 to 100
63.1 to 74
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
1.0 to 2.0
Nickel (Ni), % 0
2.0 to 5.0
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0 to 0.040
Silicon (Si), % 0
0 to 0.75
Sulfur (S), % 0 to 0.055
0 to 0.030