MakeItFrom.com
Menu (ESC)

EN 1.0070 Steel vs. B443.0 Aluminum

EN 1.0070 steel belongs to the iron alloys classification, while B443.0 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.0070 steel and the bottom bar is B443.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
43
Elastic (Young's, Tensile) Modulus, GPa 190
70
Elongation at Break, % 9.1
4.9
Fatigue Strength, MPa 210
55
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
26
Shear Strength, MPa 440
110
Tensile Strength: Ultimate (UTS), MPa 740
150
Tensile Strength: Yield (Proof), MPa 350
50

Thermal Properties

Latent Heat of Fusion, J/g 250
470
Maximum Temperature: Mechanical, °C 400
170
Melting Completion (Liquidus), °C 1470
620
Melting Onset (Solidus), °C 1430
600
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 53
150
Thermal Expansion, µm/m-K 12
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
38
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
130

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
9.5
Density, g/cm3 7.9
2.7
Embodied Carbon, kg CO2/kg material 1.4
8.0
Embodied Energy, MJ/kg 18
150
Embodied Water, L/kg 45
1130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
5.6
Resilience: Unit (Modulus of Resilience), kJ/m3 320
18
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
52
Strength to Weight: Axial, points 26
15
Strength to Weight: Bending, points 23
23
Thermal Diffusivity, mm2/s 14
61
Thermal Shock Resistance, points 23
6.8

Alloy Composition

Aluminum (Al), % 0
91.9 to 95.5
Copper (Cu), % 0
0 to 0.15
Iron (Fe), % 99.876 to 100
0 to 0.8
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0
0 to 0.35
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.055
0
Silicon (Si), % 0
4.5 to 6.0
Sulfur (S), % 0 to 0.055
0
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 0.35
Residuals, % 0
0 to 0.15