EN 1.0070 Steel vs. CR004A Copper

EN 1.0070 steel belongs to the iron alloys classification, while CR004A copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0070 steel and the bottom bar is CR004A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 9.1
15
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
43
Tensile Strength: Ultimate (UTS), MPa 740
220
Tensile Strength: Yield (Proof), MPa 350
130

Thermal Properties

Latent Heat of Fusion, J/g 250
210
Maximum Temperature: Mechanical, °C 400
200
Melting Completion (Liquidus), °C 1470
1090
Melting Onset (Solidus), °C 1430
1040
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 53
380
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.8
100
Electrical Conductivity: Equal Weight (Specific), % IACS 7.8
100

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
31
Density, g/cm3 7.9
9.0
Embodied Carbon, kg CO2/kg material 1.4
2.6
Embodied Energy, MJ/kg 18
41
Embodied Water, L/kg 45
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
29
Resilience: Unit (Modulus of Resilience), kJ/m3 320
76
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 26
6.8
Strength to Weight: Bending, points 23
9.0
Thermal Diffusivity, mm2/s 14
110
Thermal Shock Resistance, points 23
7.8

Alloy Composition

Bismuth (Bi), % 0
0 to 0.00050
Copper (Cu), % 0
99.9 to 100
Iron (Fe), % 99.876 to 100
0
Lead (Pb), % 0
0 to 0.0050
Nitrogen (N), % 0 to 0.014
0
Oxygen (O), % 0
0 to 0.040
Phosphorus (P), % 0 to 0.055
0
Silver (Ag), % 0
0 to 0.015
Sulfur (S), % 0 to 0.055
0