EN 1.0213 Steel vs. EN 1.0591 Cast Steel

Both EN 1.0213 steel and EN 1.0591 cast steel are iron alloys. Their average alloy composition is basically identical. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0213 steel and the bottom bar is EN 1.0591 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 25
19
Fatigue Strength, MPa 160 to 240
240
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 320 to 430
620
Tensile Strength: Yield (Proof), MPa 220 to 330
360

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1470
1470
Melting Onset (Solidus), °C 1430
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
53
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.7
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 46
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 33 to 98
100
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 300
340
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 11 to 15
22
Strength to Weight: Bending, points 13 to 16
20
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 10 to 14
20

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0.060 to 0.1
0
Iron (Fe), % 99.245 to 99.67
99.935 to 100
Manganese (Mn), % 0.25 to 0.45
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.1
0
Sulfur (S), % 0 to 0.025
0 to 0.030