EN 1.0214 Steel vs. EN 1.4889 Cast Nickel
EN 1.0214 steel belongs to the iron alloys classification, while EN 1.4889 cast nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.0214 steel and the bottom bar is EN 1.4889 cast nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 12 to 31 | |
| 3.4 |
| Fatigue Strength, MPa | 160 to 250 | |
| 110 |
| Poisson's Ratio | 0.29 | |
| 0.27 |
| Shear Modulus, GPa | 73 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 460 | |
| 500 |
| Tensile Strength: Yield (Proof), MPa | 210 to 360 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1160 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1360 |
| Melting Onset (Solidus), °C | 1420 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 55 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 8.5 |
| Embodied Energy, MJ/kg | 18 | |
| 120 |
| Embodied Water, L/kg | 46 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 34 to 130 | |
| 14 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 340 | |
| 180 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 12 to 16 | |
| 18 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 18 |
| Thermal Shock Resistance, points | 11 to 14 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.060 | |
| 0 |
| Carbon (C), % | 0.080 to 0.12 | |
| 0.35 to 0.45 |
| Chromium (Cr), % | 0 | |
| 32.5 to 37.5 |
| Iron (Fe), % | 99.17 to 99.6 | |
| 10.5 to 21.2 |
| Manganese (Mn), % | 0.3 to 0.5 | |
| 1.0 to 1.5 |
| Nickel (Ni), % | 0 | |
| 42 to 46 |
| Niobium (Nb), % | 0 | |
| 1.5 to 2.0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.1 | |
| 1.5 to 2.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.030 |