EN 1.0214 Steel vs. EN 1.7357 Steel

Both EN 1.0214 steel and EN 1.7357 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0214 steel and the bottom bar is EN 1.7357 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 97 to 130
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 31
23
Fatigue Strength, MPa 160 to 250
260
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 330 to 460
590
Tensile Strength: Yield (Proof), MPa 210 to 360
360

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
430
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
41
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.6
Embodied Energy, MJ/kg 18
21
Embodied Water, L/kg 46
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 34 to 130
120
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 340
340
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 12 to 16
21
Strength to Weight: Bending, points 14 to 17
20
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 11 to 14
17

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0.080 to 0.12
0.15 to 0.2
Chromium (Cr), % 0
1.0 to 1.5
Iron (Fe), % 99.17 to 99.6
96 to 97.9
Manganese (Mn), % 0.3 to 0.5
0.5 to 1.0
Molybdenum (Mo), % 0
0.45 to 0.65
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.1
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.030