EN 1.0214 Steel vs. CC497K Bronze
EN 1.0214 steel belongs to the iron alloys classification, while CC497K bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.0214 steel and the bottom bar is CC497K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 97 to 130 | |
| 55 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 93 |
| Elongation at Break, % | 12 to 31 | |
| 6.7 |
| Poisson's Ratio | 0.29 | |
| 0.36 |
| Shear Modulus, GPa | 73 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 460 | |
| 190 |
| Tensile Strength: Yield (Proof), MPa | 210 to 360 | |
| 91 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 160 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 130 |
| Melting Completion (Liquidus), °C | 1470 | |
| 870 |
| Melting Onset (Solidus), °C | 1420 | |
| 800 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 330 |
| Thermal Conductivity, W/m-K | 53 | |
| 53 |
| Thermal Expansion, µm/m-K | 12 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.9 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.9 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 29 |
| Density, g/cm3 | 7.9 | |
| 9.3 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.0 |
| Embodied Energy, MJ/kg | 18 | |
| 48 |
| Embodied Water, L/kg | 46 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 34 to 130 | |
| 10 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 340 | |
| 45 |
| Stiffness to Weight: Axial, points | 13 | |
| 5.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 16 |
| Strength to Weight: Axial, points | 12 to 16 | |
| 5.6 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 7.8 |
| Thermal Diffusivity, mm2/s | 14 | |
| 17 |
| Thermal Shock Resistance, points | 11 to 14 | |
| 7.2 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.060 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.75 |
| Carbon (C), % | 0.080 to 0.12 | |
| 0 |
| Copper (Cu), % | 0 | |
| 67.5 to 77.5 |
| Iron (Fe), % | 99.17 to 99.6 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 18 to 23 |
| Manganese (Mn), % | 0.3 to 0.5 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 0.5 to 2.5 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 4.0 to 6.0 |
| Zinc (Zn), % | 0 | |
| 0 to 2.0 |