EN 1.0220 Steel vs. ACI-ASTM CA40F Steel

Both EN 1.0220 steel and ACI-ASTM CA40F steel are iron alloys. They have 86% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0220 steel and the bottom bar is ACI-ASTM CA40F steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110
230
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
13
Fatigue Strength, MPa 210
320
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 390
770
Tensile Strength: Yield (Proof), MPa 290
550

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
750
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
27
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
7.5
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.0
Embodied Energy, MJ/kg 18
28
Embodied Water, L/kg 46
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
94
Resilience: Unit (Modulus of Resilience), kJ/m3 230
790
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 14
28
Strength to Weight: Bending, points 15
24
Thermal Diffusivity, mm2/s 14
7.2
Thermal Shock Resistance, points 12
28

Alloy Composition

Carbon (C), % 0 to 0.16
0.2 to 0.4
Chromium (Cr), % 0
11.5 to 14
Iron (Fe), % 98.2 to 100
81.6 to 88.3
Manganese (Mn), % 0 to 1.2
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.5
Sulfur (S), % 0 to 0.045
0.2 to 0.4