EN 1.0225 Steel vs. ASTM A369 Grade FP22

Both EN 1.0225 steel and ASTM A369 grade FP22 are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0225 steel and the bottom bar is ASTM A369 grade FP22.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 140
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 6.7 to 24
20
Fatigue Strength, MPa 170 to 220
160
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 280 to 290
300
Tensile Strength: Ultimate (UTS), MPa 440 to 500
470
Tensile Strength: Yield (Proof), MPa 230 to 380
240

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 400
460
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
3.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.7
Embodied Energy, MJ/kg 18
23
Embodied Water, L/kg 46
58

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31 to 95
80
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 390
150
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16 to 18
17
Strength to Weight: Bending, points 16 to 18
17
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 14 to 16
14

Alloy Composition

Carbon (C), % 0 to 0.21
0.050 to 0.15
Chromium (Cr), % 0
1.9 to 2.6
Iron (Fe), % 98 to 100
95 to 96.9
Manganese (Mn), % 0 to 1.4
0.3 to 0.6
Molybdenum (Mo), % 0
0.87 to 1.1
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.35
0 to 0.5
Sulfur (S), % 0 to 0.045
0 to 0.025