EN 1.0225 Steel vs. EN 1.8516 Steel
Both EN 1.0225 steel and EN 1.8516 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.0225 steel and the bottom bar is EN 1.8516 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 130 to 140 | |
330 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 6.7 to 24 | |
11 |
Fatigue Strength, MPa | 170 to 220 | |
570 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
74 |
Shear Strength, MPa | 280 to 290 | |
660 |
Tensile Strength: Ultimate (UTS), MPa | 440 to 500 | |
1100 |
Tensile Strength: Yield (Proof), MPa | 230 to 380 | |
910 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
260 |
Maximum Temperature: Mechanical, °C | 400 | |
470 |
Melting Completion (Liquidus), °C | 1460 | |
1460 |
Melting Onset (Solidus), °C | 1420 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 52 | |
39 |
Thermal Expansion, µm/m-K | 12 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
7.6 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
8.7 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 1.8 | |
3.7 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
1.7 |
Embodied Energy, MJ/kg | 18 | |
22 |
Embodied Water, L/kg | 46 | |
61 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 to 95 | |
120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 390 | |
2190 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 16 to 18 | |
39 |
Strength to Weight: Bending, points | 16 to 18 | |
30 |
Thermal Diffusivity, mm2/s | 14 | |
10 |
Thermal Shock Resistance, points | 14 to 16 | |
32 |
Alloy Composition
Carbon (C), % | 0 to 0.21 | |
0.2 to 0.27 |
Chromium (Cr), % | 0 | |
3.0 to 3.5 |
Iron (Fe), % | 98 to 100 | |
94.6 to 96.1 |
Manganese (Mn), % | 0 to 1.4 | |
0.4 to 0.7 |
Molybdenum (Mo), % | 0 | |
0.5 to 0.7 |
Phosphorus (P), % | 0 to 0.045 | |
0 to 0.025 |
Silicon (Si), % | 0 to 0.35 | |
0 to 0.4 |
Sulfur (S), % | 0 to 0.045 | |
0 to 0.035 |