EN 1.0234 Steel vs. 3004 Aluminum
EN 1.0234 steel belongs to the iron alloys classification, while 3004 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.0234 steel and the bottom bar is 3004 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 100 to 140 | |
| 45 to 83 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 70 |
| Elongation at Break, % | 12 to 29 | |
| 1.1 to 19 |
| Fatigue Strength, MPa | 170 to 270 | |
| 55 to 120 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 73 | |
| 26 |
| Shear Strength, MPa | 260 to 300 | |
| 100 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 480 | |
| 170 to 310 |
| Tensile Strength: Yield (Proof), MPa | 220 to 410 | |
| 68 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 180 |
| Melting Completion (Liquidus), °C | 1460 | |
| 650 |
| Melting Onset (Solidus), °C | 1420 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 900 |
| Thermal Conductivity, W/m-K | 53 | |
| 160 |
| Thermal Expansion, µm/m-K | 12 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 42 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 9.5 |
| Density, g/cm3 | 7.9 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 8.3 |
| Embodied Energy, MJ/kg | 18 | |
| 150 |
| Embodied Water, L/kg | 46 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 36 to 130 | |
| 3.2 to 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 440 | |
| 33 to 540 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 50 |
| Strength to Weight: Axial, points | 12 to 17 | |
| 18 to 31 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 25 to 37 |
| Thermal Diffusivity, mm2/s | 14 | |
| 65 |
| Thermal Shock Resistance, points | 11 to 15 | |
| 7.6 to 13 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.060 | |
| 95.6 to 98.2 |
| Carbon (C), % | 0.13 to 0.17 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 99.02 to 99.5 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 0 | |
| 0.8 to 1.3 |
| Manganese (Mn), % | 0.35 to 0.6 | |
| 1.0 to 1.5 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |