EN 1.0234 Steel vs. ASTM A182 Grade F11 Class 2

Both EN 1.0234 steel and ASTM A182 grade F11 class 2 are iron alloys. They have a very high 97% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0234 steel and the bottom bar is ASTM A182 grade F11 class 2.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 100 to 140
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 29
22
Fatigue Strength, MPa 170 to 270
220
Poisson's Ratio 0.29
0.29
Reduction in Area, % 64 to 78
34
Shear Modulus, GPa 73
73
Shear Strength, MPa 260 to 300
340
Tensile Strength: Ultimate (UTS), MPa 350 to 480
540
Tensile Strength: Yield (Proof), MPa 220 to 410
310

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 400
430
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.6
Embodied Energy, MJ/kg 18
21
Embodied Water, L/kg 46
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 36 to 130
100
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 440
260
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 12 to 17
19
Strength to Weight: Bending, points 14 to 17
19
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 11 to 15
16

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0.13 to 0.17
0.1 to 0.2
Chromium (Cr), % 0
1.0 to 1.5
Iron (Fe), % 99.02 to 99.5
95.8 to 97.7
Manganese (Mn), % 0.35 to 0.6
0.3 to 0.8
Molybdenum (Mo), % 0
0.44 to 0.65
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.1
0.5 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.040