EN 1.0234 Steel vs. EN 1.1221 Steel

Both EN 1.0234 steel and EN 1.1221 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0234 steel and the bottom bar is EN 1.1221 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 100 to 140
210 to 250
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 29
10 to 21
Fatigue Strength, MPa 170 to 270
240 to 340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 260 to 300
450 to 520
Tensile Strength: Ultimate (UTS), MPa 350 to 480
730 to 870
Tensile Strength: Yield (Proof), MPa 220 to 410
390 to 550

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
48
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 18
19
Embodied Water, L/kg 46
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 36 to 130
67 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 440
410 to 800
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 12 to 17
26 to 31
Strength to Weight: Bending, points 14 to 17
23 to 26
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 11 to 15
23 to 28

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0.13 to 0.17
0.57 to 0.65
Chromium (Cr), % 0
0 to 0.4
Iron (Fe), % 99.02 to 99.5
97.1 to 98.8
Manganese (Mn), % 0.35 to 0.6
0.6 to 0.9
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0
0 to 0.4
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.1
0 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.035