EN 1.0234 Steel vs. CC380H Copper-nickel
EN 1.0234 steel belongs to the iron alloys classification, while CC380H copper-nickel belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.0234 steel and the bottom bar is CC380H copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 100 to 140 | |
| 80 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 12 to 29 | |
| 26 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 47 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 480 | |
| 310 |
| Tensile Strength: Yield (Proof), MPa | 220 to 410 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 220 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1130 |
| Melting Onset (Solidus), °C | 1420 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 53 | |
| 46 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 36 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.8 |
| Embodied Energy, MJ/kg | 18 | |
| 58 |
| Embodied Water, L/kg | 46 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 36 to 130 | |
| 65 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 440 | |
| 59 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 12 to 17 | |
| 9.8 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 12 |
| Thermal Diffusivity, mm2/s | 14 | |
| 13 |
| Thermal Shock Resistance, points | 11 to 15 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.060 | |
| 0 to 0.010 |
| Carbon (C), % | 0.13 to 0.17 | |
| 0 |
| Copper (Cu), % | 0 | |
| 84.5 to 89 |
| Iron (Fe), % | 99.02 to 99.5 | |
| 1.0 to 1.8 |
| Lead (Pb), % | 0 | |
| 0 to 0.030 |
| Manganese (Mn), % | 0.35 to 0.6 | |
| 1.0 to 1.5 |
| Nickel (Ni), % | 0 | |
| 9.0 to 11 |
| Niobium (Nb), % | 0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |